Jotamastic 87 GF

Product description

A two component surface tolerant, glass flake reinforced, abrasion resistant, high solids epoxy mastic coating which may be applied in high film thickness. Available with different hardeners for varying substrate temperatures, Standard (Std) and Wintergrade (WG). This product is a part of a complete system which is certified not to spread flames.

Recommended use

Steel where blast cleaning may not be possible and on hydro jetted surfaces still being moist where gloss and colour retention is of minor importance. Can be used alone or in combination with various systems of primers and topcoats. Gives excellent corrosion protection both in salt and fresh water. If exposed to sunlight chalking may occur. Glass Flakes improve abrasion resistance and general wear and tear characteristics.

 

 

Film thickness and spreading rate

Std Comp. B

 

Minimum

 

Maximum

 

Typical

Film thickness, dry (µm)

200

350

250

Film thickness, wet (µm)

250

440

315

Theoretical spreading rate (m²/l)

4

2,3

3,2

 

WG Comp. B

Film thickness, dry (µm)

 

Minimum

 

200

 

Maximum

 

300

 

Typical

250

Film thickness, wet (µm)

285

430

360

Theoretical spreading rate (m²/l)

3,5

2,3

2,8

Physical properties

Colour Grey, Red, White

Solids (vol %)* 80 ± 2 Std Comp.B 70 ± 2 WG Comp.B

Flash point Std Comp. B:

35ºC ± 2 (Setaflash)

WG Comp. B:

31ºC ± 2 (Setaflash)

VOC 2,09 lbs/gal (250 gms/ltr) USA-EPA Method 24

170 gms/ltr UK-PG6/23(97). Appendix 3

Gloss Semigloss

Gloss retention Fair

Water resistance Excellent

Abrasion resistance Excellent

Solvent resistance Good

Chemical resistance Very good

Flexibility Good

*Measured according to ISO 3233:1998 (E)

Hong Kong rules:

Category of paints - Other vessel coatings; VOC 250 gms/ltr HK EPD method (Ready to use); Exempt compound - N/A; Specific gravity: 1.41 (A+B); Both VOC and Specific gravity values provided are typical values, subject to changes when different colour involved.

Surface preparation

All surfaces should be clean and free from contamination. The surface should be assessed and treated in accordance with ISO 8504.

Bare steel

Cleanliness: Power tool cleaning to min. St 2, mill scale free (ISO 8501-1:2007). Improved surface treatment (blast cleaning to Sa 2½) will improve the performance. In case of waterjetting the flash rust degree shall not exceed M (moderate) in SSPC and NACE standards for waterjetted surfaces.

Shopprimed steel

Clean, dry and undamaged approved shopprimer.

Coated surfaces

Clean, dry and undamaged compatible primer. Contact your local Jotun office for more information. For maintenance UHPWJ to WJ2 (NACE No.5/SSPC-SP 12) or Power tool cleaning to min. St 2 for rusted areas

Other surfaces

The coating may be used on other substrates. Please contact your local Jotun office for more information.

Condition during application

The temperature of the substrate should be minimum +10°C (Std) (-5°C in WG) and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is required in confined areas to ensure proper drying.

 

Hydrojetting of steel surface makes a wet surface. The surrounding air must have a relative humidity not exceeding 85

%. Before painting the surface shall not be glossy with moisture, but can have a patchy appearance.

Application methods

Spray Use airless spray

Brush Recommended for stripe coating and small areas, care must be taken to achieve the specified dry film thickness.

Roller May be used for small areas but not recommended for first primer coat, however when using roller application care must be taken to apply sufficient material in order to achieve the specified dry film thickness.

Application data

Mixing ratio (volume) Std Comp. B:

6:1

WG Comp. B:

4:1

Mixing 6 parts Comp. A (base) to be mixed thoroughly with 1 part Jotamastic 87, Std Comp. B (curing agent).

4 parts Comp. A (base) to be mixed thoroughly with 1 part Jotamastic 87, WG Comp. B. (curing agent).

Induction time 10 minutes.

Pot life (23°C) Std Comp. B:

10°C: 4 hours, 23°C: 2 hours, 40°C: 1 hour

WG Comp. B:

1 hour

Thinner/Cleaner Jotun Thinner No. 17

Guiding data airless spray

Pressure at nozzle 15 MPa (150 kp/cm², 2100 psi).

Nozzle tip 0.63-1.09 mm (0.025-0.043")

Spray angle 40-80°

Filter Filters to be removed prior to spraying.

Note * The temperature of the mixture of base and curing agent is recommended to be at least 15°C, otherwise extra solvent may be required to obtain correct viscosity.

  • Too much solvent results in lower sag resistance and slower cure.

  • If extra solvent is necessary, this should be added after mixing of the two components.

Drying time

Drying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:

  • Good ventilation (Outdoor exposure or free circulation of air)

  • Typical film thickness

  • One coat on top of inert substrate

 

Std Comp. B Substrate temperature Surface dry

Through dry Cured

Dry to recoat, minimum

   

 

10°C

18 h

24 h

14 d

 

24 h

 

23°C

7 h

10 h

7 d

 

10 h

 

40°C

2 h

4 h

2 d

 

4 h

Dry to recoat, maximum 1

   

-

-

-

 

WG Comp. B Substrate temperature

 

-5°C

 

0°C

 

5°C

 

10°C

 

23°C

Surface dry

24h

18h

12h

6 h

3,5 h

Through dry

80h

44h

26h

16 h

6 h

Cured

21d

14d

7 d

3 d

2 d

Dry to recoat, minimum

80h

44h

26h

16 h

6 h

Dry to recoat, maximum 1

         

1. Provided the surface is free from chalking and other contamination prior to application, there is normally no overcoating time limit. Best intercoat adhesion occurs, however, when the subsequent coat is applied before preceding coat has cured. If the coating has been exposed to direct sunlight for some time, special attention must be paid to surface cleaning and mattening/removal of the surface layer in order to obtain good adhesion.

The given data must be considered as guidelines only. The actual drying time/times before recoating may be shorter or longer, depending on film thickness, ventilation, humidity, underlying paint system, requirement for early handling and mechanical strength etc. A complete system can be described on a system sheet, where all parameters and special conditions could be included.

 

 

Typical paint system

 

Jotamastic 87 GF

Hardtop AS/XP

2 x 250 µm

1 x 50 µm

(Dry Film Thickness)

(Dry Film Thickness)

Other systems may be specified, depending on area of use

Storage

The product must be stored in accordance with national regulations. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed.

Handling

Handle with care. Stir well before use.

Packing size

18.7 litre unit: 16 litres Comp. A (base) in a 20 litre container and 2.7 litres Jotamastic 87, Std Comp. B (curing agent) in a 3 litre container.

20 litre unit: 16 litres Comp. A (base) in a 20 litre container and 4 litres Jotamastic 87, WG Comp. B (curing agent) in a 5 litre container.

Health and safety

Please observe the precautionary notices displayed on the container. Use under well ventilated conditions. Do not breathe or inhale mist. Avoid skin contact. Spillage on the skin should immediately be removed with suitable cleanser, soap and water. Eyes should be well flushed with water and medical attention sought immediately.

 

Скачать: 
.