Barrier

Product description

Barrier is a two-pack zinc rich epoxy primer with a high content of zinc that complies with the compositional requirements for SSPC Paint 20 level 2 and ISO 12944. Barrier is supplied with ASTM D520 Type II zinc dust.

Recommended use

As a zinc rich primer on blast cleaned steel. Barrier is used in combination with advanced coating systems to further improve protection against corrosion.

Film thickness and spreading rate

                                                                           Minimum                    Maximum                    Typical

Film thickness, dry (µm)                                 25                                 125                              75

Film thickness, wet (µm)                                45                                 235                             135

Theoretical spreading rate (m²/l)               21,2                                4,2                                 7

Comments

DFT exceeding 150 µm should be avoided.

Approvals

Australian APAS approved to specification 2916.

Physical properties

Colour Grey

Solids (vol %)* 53 ± 2

Flash point 27ºC ± 2 (Setaflash)

 

VOC 415 gms/ltr UK-PG6/23(97). Appendix 3

Gloss Flat

Water resistance Excellent

Abrasion resistance Very good

Solvent resistance Very good

Flexibility Good

*Measured according to ISO 3233:1998 (E)

Surface preparation

All surfaces should be clean, dry and free from contamination. The surface should be assessed and treated in accordance with ISO 8504.

Bare steel

Cleanliness: Blast cleaning to min. Sa 2 ½ (ISO 8501-1:2007) or for maintenance UHPWJ to WJ2 (NACE No.5/SSPC- SP 12). Roughness: using abrasives suitable to achieve minimum grade Fine (ISO 8503-2).

Shopprimed steel

Clean, dry and undamaged approved shopprimer.

Other surfaces

The coating may be used on other substrates. Please contact your local Jotun office for more information.

Condition during application

The temperature of the substrate should be minimum 5°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is required in confined areas to ensure correct drying.

Application methods

Spray Use airless spray

Brush Recommended for stripe coating and small areas, care must be taken to achieve the specified dry film thickness.

Application data

Mixing ratio (volume) 3:1

Mixing Mix 3 part Comp. A (base) thoroughly with 1 part Barrier/Barrier 77, Comp. B (curing agent).

Induction time 30 minutes.

Pot life (23°C) 24 hours. (Reduced at higher temp.).

Thinner/Cleaner Jotun Thinner No. 17

Guiding data airless spray

Pressure at nozzle 15 MPa min (150 kp/cm², 2100 psi.).

Nozzle tip 0.38 - 0.53 mm (0.015 - 0.021").

Spray angle 40 - 80°

Filter Check to ensure that filters are clean.

Drying time

Drying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:

  • Good ventilation (Outdoor exposure or free circulation of air)

  • Typical film thickness

  • One coat on top of inert substrate

 

Substrate temperature

5°C

10°C

23°C

40°C

Surface dry

50min

20min

10min

4min

Through dry

3h

2 h

1,5 h

40min

Cured

Dry to recoat, minimum 1

Dry to recoat, maximum 1,2

           10 d

 

3h

7 d

 

2 h

5 d

 

1,5 h

          2 d

 

40min

 

  1. Recommended data given for recoating with coatings normally specified on top of zinc epoxy coatings.

  2. The surface should be dry and free from any contamination prior to application of the subsequent coat.

 

The given data must be considered as guidelines only. The actual drying time/times before recoating may be shorter or longer, depending on film thickness, ventilation, humidity, underlying paint system, requirement for early handling and mechanical strength etc. A complete system can be described on a system sheet, where all parameters and special conditions could be included.

Typical paint system

Barrier 1 x 25 - 75 µm (Dry Film Thickness)

Subsequent coating(s) by choice e.g.: epoxy, acrylic or vinyl.

Other systems may be specified, depending on area of use

Storage

The product must be stored in accordance with national regulations. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed.

Handling

Handle with care. Stir well before use. Continuous stirring during application will prevent the heavy zinc pigment from settling.

Packing size

4 litre unit: 3 litres Comp. A (base) in a 5 litre container and 1 litre Barrier/Barrier 77, Comp. B (curing agent) in a 1 litre container.

or

9 litre unit: 6.75 litres Comp. A (base) in a 10 litre container and 2.25 litres Barrier/Barrier 77, Comp. B (curing agent) in a 3 litre container.

Health and safety

Please observe the precautionary notices displayed on the container. Use under well ventilated conditions. Do not breathe or inhale mist. Avoid skin contact. Spillage on the skin should immediately be removed with suitable cleanser, soap and water. Eyes should be well flushed with water and medical attention sought immediately.

 

 