Jotaguard 690

Product description

Jotaguard 690 is a two-pack, high solids polyamine cured pure epoxy based primer coating with excellent mechanical properties.

Recommended use

As a premium performance epoxy based coating to limit mechanical damage and subsequent corrosion. Particularly suitable for use as a cargo hold coating.

Film thickness and spreading rate

                                                                                                    Minimum                         Maximum                          Typical

Film thickness, dry (µm)                                                          100                                     250                                   125

Film thickness, wet (µm)                                                         135                                     335                                   165

Theoretical spreading rate (m²/l)                                           7,5                                       3                                         6

Comments

For DFTs below 150 µm thinner should be used.

Physical properties

Colour Grey, Red

Solids (vol %)* 75 ± 2

Flash point 33ºC ± 2 (Setaflash)

VOC 1,75 lbs/gal (210 gms/ltr) USA-EPA Method 24

225 gms/ltr UK-PG6/23(97). Appendix 3

Gloss Semigloss

Gloss retention Fair

Water resistance Very good

Abrasion resistance Excellent

Solvent resistance Excellent

Chemical resistance Excellent

Flexibility Good

Compatibility with

cathodic protection Good

*Measured according to ISO 3233:1998 (E)

Hong Kong rules: Category of paints - Other vessel coatings; VOC 225 gms/ltr HK EPD method (Ready to use); Exempt compound - N/A; Specific gravity: 1,59 kg/ltr (A+B); Both VOC and Specific gravity values provided are typical values, subject to changes when different colour involved.

Surface preparation

All surfaces should be clean, dry and free from contamination. The surface should be assessed and treated in accordance with ISO 8504.

Bare steel

Cleanliness: Blast-cleaning to Sa 2½ (ISO-8501-1:2007).

Shopprimed steel

Clean, dry and undamaged approved shopprimer.

Coated surfaces

Clean, dry and undamaged compatible primer. Please contact your local Jotun office for more information.

Other surfaces

The coating may be used on other substrates. Please contact your local Jotun office for more information.

Condition during application

The temperature of the substrate should be minimum -5°C and minimum 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is required in confined areas to ensure proper drying. Do not use heated air until the solvents have evaporated from the paint film to avoid surface drying and solvent entrapment. The coating should not be exposed to strain until cured.

Application methods

Spray Use airless spray

Brush Recommended for stripe coating and small areas, care must be taken to achieve the specified dry film thickness.

Roller May be used for small areas but not recommended for first primer coat, however when using roller application care must be taken to apply sufficient material in order to achieve the specified dry film thickness.

Application data

Mixing ratio (volume) 3:1

Mixing 3 parts Comp. A (base) to be mixed thoroughly with 1 part Jotaguard 690/690 S, Comp. B (curing agent).

Pot life (23°C) 1 hour (reduced at higher temperatures)

Thinner/Cleaner Jotun Thinner No. 17

Guiding data airless spray

Pressure at nozzle 15 MPa (150 kp/cm², 2100 psi)

Nozzle tip 0.43-0.64 mm (0.017-0.025")

Spray angle 40-80°

Filter Check to ensure that filters are clean.

Drying time

Drying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:

• Good ventilation (Outdoor exposure or free circulation of air)

• Typical film thickness

• One coat on top of inert substrate

1. The earliest time that it is possible to exert mechanical strain on the coating, i.e. walk on to recoat.

2. The earliest time for recoating with the same generic type of paint. Note that the paint film is not hard at this time and can not withstand mechanical strain.

3. Provided the surface is free from chalking and other contamination prior to application, there is normally no overcoating time limit. Best intercoat adhesion occurs, however, when the subsequent coat is applied before preceding coat has cured. If the coating has been exposed to direct sunlight for some time, special attention must be paid to surface cleaning and mattening/removal of the surface layer in order to obtain good adhesion.

The given data must be considered as guidelines only. The actual drying time/times before recoating may be shorter or longer, depending on film thickness, ventilation, humidity, underlying paint system, requirement for early handling and mechanical strength etc. A complete system can be described on a system sheet, where all parameters and special conditions could be included.

Typical paint system

In cargo holds:

Other systems may be specified, depending on area of use

Storage

The product must be stored in accordance with national regulations. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed.

Handling

Handle with care. Stir well before use.

Packing size

20 litre unit: 15 litres Jotaguard 690 Comp. A in a 20 litre container and 5 litres Jotaguard 690/ 690 S, Comp. B in a 5 litre container.

Health and safety

Please observe the precautionary notices displayed on the container. Use under well ventilated conditions. Do not breathe or inhale mist. Avoid skin contact. Spillage on the skin should immediately be removed with suitable cleanser, soap and water. Eyes should be well flushed with water and medical attention sought immediately.