Solvalitt is a heat resisting paint based on silicone acrylic binder.
To be used as a topcoat on items exposed to high temperatures (up to 600ºC) in combination with Zinc Silicate coatings, maximum 400ºC.
Film thickness and spreading rate Aluminium |
Minimum |
Maximum |
Typical |
Film thickness, dry (µm) |
20 |
30 |
20 |
Film thickness, wet (µm) |
55 |
80 |
55 |
Theoretical spreading rate (m²/l) |
19 |
12,7 |
19 |
Colours Film thickness, dry (µm) |
Minimum
20 |
Maximum
30 |
Typical
20 |
Film thickness, wet (µm) |
50 |
70 |
50 |
Theoretical spreading rate (m²/l) |
21 |
14 |
21 |
4,43 lbs/gal (530 gms/ltr) USA-EPA Method 24
500 gms/ltr UK-PG6/23(97). Appendix 3
4,34 lbs/gal (520 gms/ltr) USA-EPA Method 24
490 gms/ltr UK-PG6/23(97). Appendix 3
Gloss Aluminium sheen/Flat
*Measured according to ISO 3233:1998 (E)
Other colours (limited range) can be supplied on request and may be subject to maximum temperature limitations below 600 °C depending on specific pigments heat resistance.
Please consult with Jotun local office for detail.
All surfaces should be clean, dry and free from contamination. The surface should be assessed and treated in accordance with ISO 8504.
Cleanliness: Blast cleaning to Sa 2½ (ISO 8501-1:2007). Roughness: using abrasives suitable to achieve grade Fine to Medium G (30-85 µm, Ry5) (ISO 8503-2)
Cured and clean zinc silicate primer.
The coating may be used on other substrates. Please contact your local Jotun office for more information.
The temperature of the substrate should be minimum 3ºC above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to ensure correct drying.
Thinner/Cleaner Jotun Thinner No. 7
Pressure at nozzle 15 MPa (150 kp/cm², 2100 psi).
Nozzle tip 0.38-0.48 mm (0.015-0.021")
Filter Check to ensure that filters are clean.
Drying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:
Good ventilation (Outdoor exposure or free circulation of air)
Typical film thickness
One coat on top of inert substrate
Substrate temperature |
5°C |
10°C |
23°C |
40°C |
Surface dry |
60min |
45min |
30min |
15min |
Through dry |
4 h |
3 h |
2 h |
1,5 h |
Dry to recoat, minimum Dry to recoat, maximum 1 |
8 h |
5 h |
4 h |
3 h |
1. The surface should be dry and free from any contamination prior to application of the subsequent coat.
The given data must be considered as guidelines only. The actual drying time/times before recoating may be shorter or longer, depending on film thickness, ventilation, humidity, underlying paint system, requirement for early handling and mechanical strength etc. A complete system can be described on a system sheet, where all parameters and special conditions could be included.
Typical paint system |
||
Resist 78, Resist 86 or Resist GTI Solvalitt or Solvalitt |
1 x 75 µm 1 - 2 x 20 µm
2 - 3 x 20 µm |
(Dry Film Thickness) (Dry Film Thickness)
(Dry Film Thickness) |
Other systems may be specified, depending on area of use
Storage condition are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed. The container must be protected from freezing.
SHELF LIFE: 2 years at 23°C, subject to re-inspection thereafter. Storage at elevated temperatures will reduce product shelf life significantly.
Handle with care. Stir well before use.
5 litre container
Please observe the precautionary notices displayed on the container. Use under well ventilated conditions. Do not breathe or inhale mist. Avoid skin contact. Spillage on the skin should immediately be removed with suitable cleanser, soap and water. Eyes should be well flushed with water and medical attention sought immediately.